PVDF美国苏威TA-11008---PVDF美国苏威11008/0001---长期销售大量PVDF美国苏威TA-11008/0001---物理性能额定值(公制)额定值(英制)测试方法密度1.78g/cc0.0643lb/in³ISO1183吸水率24hr@23°C;ISO62(method1)MeltIndexofCompound8.0g/10min@Load2.16kg,Temperature230°C8.0g/10min@Load4.76lb,Temperature446°FASTMD123824g/10min@Load5.00kg,Temperature230°C24g/10min@Load11.0lb,Temperature446°FASTMD1238机械性能额定值(公制)额定值(英制)测试方法抗张强度(断裂)47.0MPa6820psi50mm/min;ASTMD638伸长率(断裂)600%600%50mm/min;ASTMD638弯曲模量1.00GPa145ksi2mm/min;ASTMD790热性能额定值(公制)额定值(英制)测试方法熔融温度160°C320°FCrystallinitybyDSC;ASTMD3418材料描述测试方法形式GranulesPVDFisidealformultipleapplicati***acrossawidearrayofindustries.Widelyusedinthechemicalprocessing,wireandcable,semiconductor,andoilandgasindustries.PVDFisalsogainingrecognitioninautomotive,building,electronics,foodprocessing,pharmaceuticalandbatteryapplicati***.PVDF11008/0001combinesexcellentchemicalresistance,dimensionalstabilityandexcellentflameand***okeresistancewithamoderatedegreeofflexibility.(Forapplicati***requiringhighdegreesofflexibility,seeour30000seriescopolymers.)PVDF11008/0001hassetthestandardforplenumratingjacketingandtubes,c***istentlyachievingUL150°Cratinginnumerouscablec***tructi***andfiberracewaydesigns.FeaturesandBenefits:PVDF11008/0001isacopolymerofVF2andHFP(hexafluoropropylene)ImprovedflexibilityoverPVDFhomopolymersIdealforapplicati***wherehighstrengthandamoderatedegreeofflexibilityarerequiredIdealforhighspeedextrusionExcellentweatherabilityGoodchemicalresistanceLongtermusetemperaturesupto150°C(302ºF)Processableusingmostconventionalthermoplasticconversiontechniques)