Solef6008---PVDF美国苏威6008---长期代理销售PVDF美国苏威6008/0001---特性低粘度均聚物加工方法***成型物理性能额定值单位制测试方法比重1.75到1.80g/cm³ASTMD792熔流率（熔体流动速率）ASTMD1238230°C/2.16kg5.5到11g/10minASTMD1238230°C/5.0kg16到30g/10minASTMD1238收缩率-流动2.0到3.0%吸水率(23°C,24hr)%ASTMD570硬度额定值单位制测试方法肖氏硬度(邵氏D,1秒,2.00mm)73到80ASTMD2240机械性能额定值单位制测试方法拉伸模量1(23°C,2.00mm)1800到2500MPaASTMD638抗张强度2ASTMD638屈服,23°C,2.00mm50.0到60.0MPaASTMD638断裂,23°C,2.00mm30.0到50.0MPaASTMD638伸长率3ASTMD638屈服,23°C,2.00mm5.0到10%ASTMD638断裂,23°C,2.00mm20到300%ASTMD638摩擦系数ASTMD1894与自身-动态0.15到0.35ASTMD1894与自身-静态0.20到0.40ASTMD1894泰伯耐磨性(1000Cycles,1000g,CS-10转轮)5.00到10.0mgASTMD4060冲击性能额定值单位制测试方法简支梁缺口冲击强度4(23°C,4.00mm)40.0到120J/mASTMD6110热性能额定值单位制测试方法玻璃转化温度-40.0°CASTMD4065维卡软化温度135到145°CASTMD15255熔融温度170到175°CASTMD3418结晶峰温度(DSC)134到144°CASTMD3418线形热膨胀系数-流动(0到40°C)1.4E-4cm/cm/°CASTMD696比热ASTME96823°C1200J/kg/°CASTME968100°C1600J/kg/°CASTME968导热系数(23°C)0.20W/m/KASTMC177结晶热54.0到60.0J/gASTMD3417融合热量58.0到67.0J/gASTMD3417电气性能额定值单位制测试方法表面电阻率>1.0E+14ohmsASTMD257体积电阻率>1.0E+14ohms·cmASTMD257介电强度(23°C,1.00mm)20到25kV/mmASTMD149介电常数(23°C,1kHz)7.00到10.0ASTMD150可燃性额定值单位制测试方法UL阻燃等级(0.200mm)V-0UL94极限氧指数(3.00mm)44%ASTMD2863---***长期销售大量PVDF美国苏威6008/0001)