SABICCU6800PC+ABS物性表怎么选料请T&V:153-3800-1126T:170-8463-1798物理性能额定值(公制)额定值(英制)测试方法比重1.20g/cc1.20g/ccASTMD792线性成型收缩率,Flow0.0050-0.0070cm/cm@Thickness3.20mm0.0050-0.0070in/in@Thickness0.126inSABICMethod熔体流动速率23g/10min@Load2.16kg,Temperature260°C23g/10min@Load4.76lb,Temperature500°FASTMD123881g/10min@Load5.00kg,Temperature260°C81g/10min@Load11.0lb,Temperature500°FASTMD1238机械性能额定值(公制)额定值(英制)测试方法抗张强度(断裂)46.0MPa6670psiTypeI,50mm/min;ASTMD638抗张强度(屈服)59.0MPa8560psiTypeI,50mm/min;ASTMD638伸长率(断裂)66%66%TypeI,50mm/min;ASTMD638屈服伸长率3.3%3.3%TypeI,50mm/min;ASTMD638拉伸模量2.99GPa434ksi50mm/min;ASTMD638弯曲强度88.0MPa12800psi1.3mm/min,50mmspan;ASTMD790弯曲模量2.52GPa365ksi1.3mm/min,50mmspan;ASTMD790悬壁梁缺口冲击强度5.17J/cm9.69ft-lb/inASTMD256落锤总能量47.0J@Temperature23.0°C34.7ft-lb@Temperature73.4°FASTMD3763热性能怎么选料请T&V:153-3800-1126T:170-8463-1798额定值(公制)额定值(英制)测试方法线形热膨胀系数-流动75.6µm/m-°C@Temperature-40.0-40.0°C42.0µin/in-°F@Temperature-40.0-104°FASTME831线性热膨胀系数,横向流动75.6µm/m-°C@Temperature-40.0-40.0°C42.0µin/in-°F@Temperature-40.0-104°FASTME831载荷下热变形温度(0.46MPa)88.0°C@Thickness3.20mm190°F@Thickness0.126inunannealed;ASTMD648DeflectionTemperatureat1.8MPa(264psi)74.0°C@Thickness3.20mm165°F@Thickness0.126inunannealed;ASTMD64879.0°C@Thickness6.40mm174°F@Thickness0.252inunannealed;ASTMD648维卡软化温度98.0°C208°FRateB/50;ASTMD1525ULRTI60.0°C140°FUL746BULRTI，机械冲击60.0°C140°FUL746BULRTI，机械无冲击60.0°C140°FUL746B可燃性(UL94)V-1@Thickness2.00mmV-1@Thickness0.0787inUL945VB@Thickness2.00mm5VB@Thickness0.0787in)