SABICPC/LUX2114/***商PC/LUX2114/沙伯基础（原GE）沙伯基础（原GE）PCPC/LUX2114G/沙伯基础（原GE）沙伯基础（原GE）PC怎么选料请T&V:153-3800-1126T:170-8463-1798LUX2114PC|聚碳酸酯沙伯基础（原GE）规格级别：阻燃注塑LUX2114物性表怎么选料请T&V:153-3800-1126T:170-8463-1798物理性能额定值单位测试方法密度1.20g/cm³ASTMD7921.19g/cm³ASTMD792特定体积0.830cm³/gASTMD792熔流率((300°C/1.2kg))17.5g/10minASTMD1238收缩率-流动((3.20mm))0.50到0.70%InternalMethod吸水率(24hr)0.15%ASTMD570平衡,23°C(ASTMD570)%0.35平衡,100°C(ASTMD570)%0.58室外适用性f2UL746C硬度额定值单位测试方法洛氏硬度(M计秤)70ASTMD785(R计秤)110ASTMD785机械性能怎么选料请T&V:153-3800-1126T:170-8463-1798额定值单位测试方法抗张强度(屈服,TypeI,5mm/min)62.1MPaASTMD638(断裂,TypeI,5mm/min)65.5MPaASTMD638伸长率(屈服,TypeI,5mm/min)7.0%ASTMD638(断裂,TypeI,5mm/min)110%ASTMD638弯曲模量(50.0mm跨距,1.3mm/min)2340MPaASTMD790弯曲强度(屈服,50.0mm跨距,1.3mm/min)93.1MPaASTMD790抗泰伯磨耗((1000Cycles,1000g,CS-17转轮))10.0mgASTMD1044冲击性能额定值单位测试方法简支梁缺口冲击强度(-30°C,80*10*3sp=62mm12kJ/m²ISO179/1eA(23°C,80*10*3sp=62mm)65kJ/m²ISO179/1eA简支梁缺口冲击强度(-30°C,80*10*3sp=62mm)无断裂ISO179/1eU(23°C,80*10*3sp=62mm)无断裂ISO179/1eU悬壁梁缺口冲击强度(23°C)600J/mASTMD256(-30°C,80*10*3)11kJ/m²ISO180/1A(23°C,80*10*3)65kJ/m²ISO180/1A无缺口悬臂梁冲击(23°C)3200J/mASTMD4812(-30°C,80*10*3)无断裂ISO180/1U(23°C,80*10*3)无断裂ISO180/1U落锤冲击((23°C))169JASTMD3029拉伸冲击强度(TypeS)546kJ/m²ASTMD1822热性能怎么选料请T&V:153-3800-1126T:170-8463-1798额定值单位测试方法热变形温度(0.45MPa,未退火,6.40mm)138°CASTMD648(1.8MPa,未退火,6.40mm)132°CASTMD648维卡软化温度(标准B(120°C/h),压力2(50N))154°CASTMD1525BallPressureTest((125°C))PassIEC60695-10-2线形膨胀系数(流动:-40到95°C)0.000068cm/cm/°CASTME831比热()1260J/kg/°CASTMC351导热系数0.25W/m/KASTMC177RTIElec80.0°CUL746RTIImp80.0°CUL746RTIStr80.0°CUL746电气性能额定值单位测试方法体积电阻率>1.0E+17ohm·cmASTMD257介电强度((3.20mm,inAir))15kV/mmASTMD149介电常数(50Hz)3.17ASTMD150(60Hz)3.17ASTMD150(1MHz)2.96ASTMD150耗散因数(50Hz)0.00090ASTMD150(60Hz)0.00090ASTMD150(1MHz)0.010ASTMD150相比耐漏电起痕指数(CTI)3PLCcodeUL746A高电弧燃烧指数(HAI)1PLCcodeUL746A热丝引燃(HWI)3PLCcodeUL746A可燃性怎么选料请T&V:153-3800-1126T:170-8463-1798额定值单位测试方法UL阻燃等级(1.20mm)V-2UL94灼热丝***指数(0.750mm)750°CIEC60695-2-12(1.50mm)850°CIEC60695-2-12热灯丝点火温度(0.750mmbyVDE)875°CIEC60695-2-13(1.50mm)850°CIEC60695-2-13***额定值单位测试方法干燥温度120°C干燥时间3到4hr干燥时间.***大48hr建议的***大水分含量0.02%建议注入量40到60%螺筒后部温度260到280°C螺筒中部温度270到295°C螺筒前部温度280到305°C射嘴温度275到300°C加工(熔体)温度280到305°C模具温度70到95°C背压0.3到0.7MPa螺杆转速40到70rpm排气孔深度0.025到0.076mm)