美国(胶颗)泰科纳1140L4BK/PPS性能项目试验条件[状态]测试方法测试数据数据单位物理性能比重ASTMD792,ISO11831.65g/cm³特定体积ASTMD7920.611cm³/g收缩率流动ASTMD9550.20到0.30%横向流动ASTMD9550.50到0.70%横向流量ISO294-40.40到0.60%流量ISO294-40.20到0.60%吸水率(饱和,23°C)ISO620.020%硬度洛氏硬度M级ASTMD785100M计秤ISO2039-2100机械性能拉伸模量-40°CASTMD63814500MPa75°CASTMD63811900MPa150°CASTMD6384270MPa200°CASTMD6383240MPa--ISO527-2/1A/114700MPa抗张强度断裂,23°CASTMD638200MPa断裂ISO527-2/1A/5195MPa伸长率断裂,23°CASTMD6381.7%断裂ISO527-2/1A/51.9%弯曲模量(23°C)ISO17814500MPa弯曲应力2ISO178285MPa冲击性能简支梁缺口冲击强度-30°CISO179/1eA10kJ/m²23°CISO179/1eA10kJ/m²简支梁无缺口冲击强度-30°CISO179/1eU53kJ/m²23°CISO179/1eU53kJ/m²悬壁梁缺口冲击强度-30°CISO180/1A10kJ/m²23°CISO180/1A10kJ/m²无缺口伊佐德冲击强度(23°C)ISO180/1U34kJ/m²热性能载荷下热变形温度0.45MPa,未退火ASTMD648280°C1.8MPa,未退火ASTMD648265°C1.8MPa,未退火ISO75-2/A270°C8.0MPa,未退火ISO75-2/C215°C玻璃转化温度3ISO11357-290.0°C熔融温度3ISO11357-3280°C线形热膨胀系数流动ISO11359-22.6E-5cm/cm/°C横向ISO11359-24.2E-5cm/cm/°C电气性能表面电阻率IEC60093>1.0E+15ohms体积电阻率--ASTMD2571.0E+16ohms·cm--IEC60093>1.0E+15ohms·cm介电强度IEC60243-128kV/mm介电常数1kHzASTMD1503.501MHzASTMD1503.501MHzIEC602504.10耗散因数1kHzASTMD1501.0E-31MHzASTMD1501.0E-31MHzIEC602502.0E-3耐电弧性ASTMD495134sec漏电起痕指数IEC60112125V可燃性UL阻燃等级0.38mmUL94V-01.5mmUL94V-03.0mmUL945VA极限氧指数ISO4589-247%充模分析SpecificHeatCapacityofMelt内部方法1500J/kg/°C补充信息SpecimenThickness-Shrinkage内部方法3.18mmPPS(聚苯硫醚)|1140L4|美国塞拉尼斯注塑成型时特性备注:注塑级,中等熔融粘度.PPS|Fortron®1140L4FC|美国塞拉尼斯特性备注:生产厂商：美国塞拉尼斯美国塞拉尼斯PPS|Fortron®1140L4|美国塞拉尼斯PPS|Fortron®1140L4-T|pps被广泛用于电子电器领域：电脑/电器接插件、器、线圈骨架、连接器、继电器、熔断器、调节器、温控开关、温控保护器、装饰灯座、开关插座、电磁炉底盘、电暖器出风口、散热扇翼、变压器线圈骨架、高电压大电流的高压断路开关骨架、电脑风扇、节能灯灯头、电器开关、电子镇流器外壳、电吹风、电烤箱、电饭煲、微波炉、水泵配件及电动工具配件等；汽车领域：主要用于高压无触点点火器的分电器盖、转子、点火线圈盖、接线端子、传感器盒、前后灯座、集崇路盒、微电机后盖、冷气风扇等，PBT通讯领域，主要用于程控电话的集成模块、接线板、电容器外壳、天线护套等；用途氢氧化镁广泛用于,,,,,,,,不饱和聚酯,环氧树脂,橡胶,油漆的阻燃填充剂,化工,环保等工业领域用于塑料、橡胶等高分子材料的优良阻燃剂和填充剂,在环保方面作为烟道气脱硫剂个,全年累计产品销售收入,,千元,比上年同期增长,累计利润总额达到,,千元。聚酯类、、、是属於极性高分子,其表面能较高,表面湿张力在达因厘米以上。是目前广为流行的新型纤维,是一种新型族聚酯纤维,与涤纶、是属同一家族系列的高分子物。纱线的上浆所用的浆料与涤纶一样,主浆料应选用含有多量酯基的水溶性合成高分子材料,)