热性能额定值单位制测试方法线形膨胀系数ISO11359-2流动:-40到23°C0.00010cm/cm/°C流动:23到55°C0.00011cm/cm/°C流动:55到100°C0.00015cm/cm/°C横向:-40到23°C0.00010cm/cm/°C横向:23到55°C0.00011cm/cm/°C横向:55到100°C0.00016cm/cm/°C***额定值单位制干燥温度80.0°C干燥时间-热风干燥机2.0到4.0hr建议的***大水分含量<0.20%加工（熔体）温度210到220°CMeltTemperature,Optimum-InjectionMolding215°C模具温度80.0到100°CMoldTemperature,Optimum-InjectionMolding90°C机械性能额定值单位制测试方法拉伸模量(23°C)3000MPaISO527-2拉伸应力(屈服,23°C)71.0MPaISO527-2拉伸应变(屈服,23°C)25%ISO527-2断张率(23°C)35%ISO527-2弯曲模量(23°C)2800MPaISO178冲击性能额定值单位制测试方法简支梁缺口冲击强度ISO179/1eA-30°C8.0kJ/m²23°C10kJ/m²简支梁缺口冲击强度(23°C)150kJ/m²ISO179/1eU热性能额定值单位制测试方法热变形温度0.45MPa,未退火158°CISO75-2/B1.8MPa,未退火95.0°CISO75-2/A熔融温度4178°CISO11357-3)