科思创拜耳FR3科思创拜耳FR3010PCABS010科思创拜耳FR3010PCABSMetric公制数据English英制数据Comments测试方法Density密度1.20g/cc0.0434lb/in³ISO1183MoistureAbsorptionatEquilibrium吸湿平衡0.20%0.20%23°C/50%RH;ISO62WaterAbsorptionatSaturation饱和水吸收率0.60%@Temperature23.0°C0.60%@Temperature73.4°FISO62LinearMoldShrinkage,Flow线性收缩率/流动0.0040-0.0060cm/cm0.0040-0.0060in/inontensilebar;SABICMethodMeltFlow熔体流动速率13g/10min@Load2.16kg,Temperature260°C13g/10min@Load4.76lb,Temperature500°F[cm^3/10min]MeltVolumeRate;ISO1133MechanicalProperties力学性能Metric公制数据English英制数据Comments测试方法Hardness,RockwellR罗氏硬度R122122ISO2039-2Hardness,硬度H358/30116MPa16800psiISO2039-1TensileStrengthatBreak断裂拉伸强度40.0MPa5800psi5mm/min;ISO52750.0MPa7250psi50mm/min;ISO527TensileStrength,Yield屈服拉伸强度50.0MPa7250psi5mm/min;ISO52760.0MPa8700psi50mm/min;ISO527ElongationatBreak断裂伸长率>=50%>=50%50mm/min;ISO52757%57%5mm/min;ISO527ElongationatYield屈服伸长率4.0%4.0%5mm/min;ISO5274.0%4.0%50mm/min;ISO527TensileModulus拉伸模量2.80GPa406ksi1mm/min;ISO527FlexuralYieldStrength弯曲屈服强度98.0MPa14200psi2mm/min;ISO178FlexuralModulus弯曲弹性模量2.80GPa406ksi2mm/min;ISO178IzodImpact,Notched悬臂梁缺口冲击强度(ISO)10.0kJ/m²@Temperature-30.0°C4.76ft-lb/in²@Temperature-22.0°F80*10*4;ISO180/1A)