（高密度聚乙烯）台聚HDPELH606（高密度聚乙烯）台聚HDPELH606性能项目测试条件测试方法单位数值/描述机械性能拉伸强度(引张强度)ASTMD638/ISO527kg/cm²(MPa)[Lb/in2]310断裂伸长率ASTMD638/ISO527%220拉伸模量ASTMD638/ISO527kg/cm²(MPa)[Lb/in2]--拉伸屈服伸长率(延伸率)ASTMD638/ISO527%--拉伸断裂伸长率(延伸率)ASTMD638/ISO527%--弯曲模量(弯曲弹性率)ASTMD790/ISO178kg/cm²(MPa)[Lb/in2]--弯曲强度ASTMD790/ISO178kg/cm²(MPa)[Lb/in2]9900洛氏硬度ASTMD78570IZOD缺口冲击强度1/4"23℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in--1/4"-30℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in--1/8"23℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in--1/8"-30℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in--Charpy冲击强度23℃（缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in7-30℃（缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in723℃（无缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in7-30℃（无缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in--物性性能比重（密度）ASTMD792/ISO11830.962成型收缩率ASTMD955%0.38熔融指数（流动系数）200℃/5kgASTMD1238/ISO1133g/10min6220℃/10kgASTMD1238/ISO1133g/10min6吸水率23℃/24HASTMD570/ISO62%0.002热性能热变形温度退火ASTMD648/ISO75℃（℉）105未退火ASTMD648/ISO75℃（℉）105维卡软化点ASTMD1525/ISOR306℃（℉）--熔点-℃（℉）--燃烧性（率）UL94HB线性膨胀系数ASTMD696/ISO11359mm/mm.℃--加工条件干燥条件--加工温度射嘴℃--料筒前段℃--料筒中段℃--料筒后段℃--熔体温度℃--模具温度℃--压力注塑压力Mpa--保压压力Mpa--背压Mpa--螺杆转速rpm--其他备注--颜色自郄色特性--用途射出成型，细圆丝加工)