物理性能额定值单位制测试方法比重--1.07g/cm³ASTMD792--1070kg/m³ISO11833熔流率ASTMD1238200°C/5.0kg0.50g/10min220°C/10.0kg6.0g/10min230°C/3.8kg2.0g/10min熔体体积流动速率(220°C/10.0kg)7.80cm³/10minISO11333收缩率-流动0.40到0.70%ASTMD955吸水率(饱和)0.40%ISO623硬度额定值单位制测试方法洛氏硬度(R计秤)93ASTMD785机械性能额定值单位制测试方法拉伸模量--41730MPaASTMD638--1100MPaISO527-23抗张强度屈服40.0MPaASTMD638屈服39.0MPaISO527-23伸长率屈服55.0%ASTMD638屈服5.0%ISO527-23断裂35%ASTMD638断裂伸长率28%ISO527-23弯曲模量61910MPaASTMD790弯曲强度6(屈服)64.7MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度ISO179/1eA3-30°C3.90kJ/m²23°C50.2kJ/m²简支梁冲击强度ISO179/1eU3-30°C42.2kJ/m²23°C无断裂悬壁梁缺口冲击强度ASTMD256-30°C,3.18mm59J/m-30°C,6.35mm59J/m23°C,6.35mm340J/m23°C,3.18mm440J/m热性能额定值单位制测试方法热变形温度ASTMD6480.45MPa,未退火,6.35mm96.1°C0.45MPa,退火,6.35mm102°C1.8MPa,未退火,6.35mm85.6°C1.8MPa,退火,6.35mm97.2°C玻璃转化温度7110°CISO11357-23维卡软化温度--93.3°CASTMD152550°C/h,B(50N)93.8°CISO3063线形膨胀系数ISO11359-23流动9.4E-5cm/cm/°C横向9.4E-5cm/cm/°CRTIElecUL7461.50mm50.0°C3.00mm50.0°C6.00mm50.0°CRTIImpUL7461.50mm50.0°C3.00mm50.0°C6.00mm50.0°CRTIStrUL7461.50mm50.0°C3.00mm50.0°C6.00mm50.0°C电气性能额定值单位制测试方法体积电阻率1.0E+15ohm·cmASTMD257介电强度28kV/mmASTMD149耐电弧性PLC6ASTMD495相比耐漏电起痕指数(CTI)PLC0UL746高电弧燃烧指数(HAI)UL7461.50mmPLC03.00mmPLC06.00mmPLC0高压电弧抗压指数(HVAR)(PLC)PLC1UL746热丝引燃(HWI)UL7461.50mmPLC43.00mmPLC36.00mmPLC2可燃性额定值单位制测试方法UL阻燃等级UL941.50mmHB1.59mmHB3.00mmHB3.18mmHB6.00mmHB一定厚度与小时下的阻燃等级(3.20mm,UL)HBISO12103挤出额定值单位制干燥温度85.0到95.0°C干燥时间2.0到3.0hr建议的最大水分含量0.10%第1气缸区温度190到210°C第2气缸区温度200到220°C第3气缸区温度210到230°C第4气缸区温度210到230°C第5气缸区温度210到230°C连接器温度210到230°C模具温度210到250°C牵引辊70.0到100°C背压0.0867到0.100MPa)