LI-970ASA/LG化学/LI-970适宜生产门窗型材·重要参数：熔体流动速率:12g/10min密度:1.12g/cm3成型收缩率:0.4%缺口冲击强度:14拉伸强度:44.1MPa断裂伸长率:6%弯曲强度:72.52MPa弯曲模量:2156MPa硬度:103维卡软化点:90℃热变形温度:82℃·原料技术数据·性能项目试验条件[状态]测试方法测试数据数据单位物理性能比重ASTMD7921.12模缩率3.2mmASTMD9550.4-0.7%熔体流动速率220℃/10kgASTMD123812g/10min机械性能拉伸强度3.2mm,屈服(50mm/min)ASTMD638450kg/cm2伸长率3.2mm,屈服(50mm/min)ASTMD638>6%3.2mm,断裂(50mm/min)ASTMD63825%拉伸模量3.2mm(1mm/min)ASTMD63820000kg/cm2弯曲强度3.2mm(15mm/min)ASTMD790740kg/cm2弯曲模量3.2mm(15mm/min)ASTMD79022000kg/cm2IZOD冲击强度6.4mm,缺口,23℃ASTMD25614kg.cm/cm6.4mm,缺口,-30℃ASTMD2564kg.cm/cmIZOD冲击强度3.2mm,缺口,23℃ASTMD25618kg.cm/cm3.2mm,缺口,-30℃ASTMD2564kg.cm/cm洛氏硬度RScaleASTMD785103热性能热变形温度6.4mm，未退火,18.6kgASTMD64882℃6.4mm，未退火,4.6kgASTMD64891℃维卡软化温度50kg,50℃/hASTMD152590℃阻燃性0.8mmUL94class1.6mmHBclass2.5mmclass3.2mmHBclass·)