PETGGN071产品参数性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTMD638/ISO527kg/cm²(MPa)[Lb/in2]断裂伸长率ASTMD638/ISO527180%拉伸模量ASTMD638/ISO52720387kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)ASTMD638/ISO527%拉伸断裂伸长率(延伸率)ASTMD638/ISO527%弯曲模量(弯曲弹性率)ASTMD790/ISO17821441kg/cm²(MPa)[Lb/in2]弯曲强度ASTMD790/ISO178683kg/cm²(MPa)[Lb/in2]洛氏硬度ASTMD785108IZOD缺口冲击强度1/4"23℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in1/4"-30℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in1/8"23℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in1/8"-30℃ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃（缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTMD256/ISO179kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）ASTMD792/ISO11831.27成型收缩率ASTMD9550.002-0.005%熔融指数（流动系数）200℃/5kgASTMD1238/ISO1133g/10min220℃/10kgASTMD1238/ISO1133g/10min吸水率23℃/24HASTMD570/ISO62%热性能热变形温度退火ASTMD648/ISO75℃（℉）未退火ASTMD648/ISO75158℃（℉）维卡软化点ASTMD1525/ISOR306℃（℉）熔点-℃（℉）燃烧性（率）UL94线性膨胀系数ASTMD696/ISO11359mm/mm.℃电气性能介电常数100HZ1MHZ体积电阻率Ω.cm表面电阻率Ω耐电弧性介电损耗100HZ1MHZ光学性能折射率ASTMD542/ISO489透光率ASTMD1003/ISO13468%模糊系数（Haze）ISO14782%加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速rpm其他备注颜色特性刚性良好,光泽度高,抗撞击性及韧性高用途个人护理,包装,家用货品,家具,文具,玩具.PETGGN071伊斯曼化学/高透明PETG出众的热成型性能PETG板材易于生产出造型复杂及拉伸比大的制品。而且，与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高。坚韧性PETG板材的挤出板材通常比通用压克力坚韧15至20倍，比抗冲改性的压克力坚韧5至10倍。PETG板材在加工、运输和使用过程中具有足够的承受能力，有助于防止***。耐候性PETG板材提供了***的耐候性。它可以保持产品的坚韧性，防止变黄。它含有紫外线吸收剂，可共挤成一保护层，保护了板材免受紫外线的***影响。加工简便PETG板材可进行锯切、模切、钻孔、冲孔、剪切、铆接、铣边以及冷弯，不至于破碎。表面的轻微刮痕可用热风枪来消除。溶剂粘接亦是常规操作。它比通用压克力、抗冲改性压克力或PC板更易于加工，并可进行植绒、电镀、静电等加工处理。***的耐化学性能PETG板材可以耐受多种***以及常用的清洁剂。环保PETG板材基材均为环保材料，符合食品接触管理要求。经济性它比PC板便宜，比压克力经久耐用。PETG是一种非结晶性共聚酯。在其生产过程中，由于一定数量的乙二醇被1，4-cyclohexanedimethanol(CHDM)所取代，可预防结晶化，进而改善加工制造和透明度。其制品高度透明，抗冲击性能优异，特别适宜成型厚壁透明制品，其加工成型性能***，能够按照设计者的意图进行任意形状的设计，可能采用传统的挤出、注塑、吹塑及吸塑等成型方法，可以广泛用于板材、片材、高性能收缩膜、瓶用及异型材等市场，同时其二次加工性能优良，可以进行常规机加工修饰。)