LB-L620LB-L620NLB-L690用于***Mn・Mo钢•Mn-Mo-Ni钢用LB-L620相当于AWSA5.5E9016-GLB-L620N相当于AWSA5.5E9016-GLB-L690相当于AWSA5.5E10016-G用途LB-L620:用于ASTMA302B、A533BCL1及A508CI.3等钢。LB-L620N:提高了LB-L620中Ni的含量，提高了在低温下的落锤性能。LB-L690:用于ASTMA533BCI.2等钢。使用特性熔敷金属为Mn-Mo-Ni系的低氮型全位置焊条，长时间焊后热处理后也有良好的力学性能。工艺要点①预热•层间温度:150-250%：②焊后热处理温度:590-650七③请参照212页。。熔敷金属化学成分一例(％)W号cSiPSNiMoLB-L6200.060.530.0060.0031.310.400.56LB-L620N0.060.460.0070.0031.420.740.57LB-L6900.100.380.0060.0031.180.800.44。熔敷金属力学性能一例牌号屈服强度MPa抗拉强度MPa延伸率%吸收功-12XJ热处理LB-L62057566325174620rx1hr54563926179650Tx7.5hrLB-L620N59069022160595rx8hr550650231706l5rx30hrLB-L69057867725141590rx3hr54264025163640Tx26hr。主要尺寸及推荐电流范围AC、DC(+)責径mm3.24.05.0长度mm350400400电流范囤ALB-L62090-130130-180180-240LB-L620NLB-L690立辉何WLB-L62080-120100-170一LB-L620NLB-L690)