lexanPCEXL1414物性Lexan*EXL1414polycarbonate(PC)siloxanecopolymerresinisamediumflowopaqueinjectionmolding(IM)grade.Thisresinoffersextremelowtemperature(-40C)ductilityincombinationwithexcellentprocessabilityandreleasewithopportunitiesforshorterIMcycletimescomparedtostandardPC.LexanEXL1414resinisaproduct***ailableinwiderangeofopaquecolorsandmaybeanexcellentcandidateforawidevarietyofapplicati***.PropertyTYPICALPROPERTIES(1)MECHANICALValueUnitStandardTensileStress,yld,TypeI,50mm/min560kgf/cm2ASTMD638TensileStress,brk,TypeI,50mm/min510kgf/cm2ASTMD638TensileStrain,yld,TypeI,50mm/min6%ASTMD638TensileStrain,brk,TypeI,50mm/min98%ASTMD638TensileModulus,50mm/min20500kgf/cm2ASTMD638FlexuralStress,yld,1.3mm/min,50mmspan940kgf/cm2ASTMD790FlexuralModulus,1.3mm/min,50mmspan22700kgf/cm2ASTMD790Hardness,RockwellL89-ASTMD785Hardness,RockwellR121-ASTMD785TensileStress,yield,50mm/min57MPaISO527TensileStress,break,50mm/min60MPaISO527TensileStrain,yield,50mm/min6%ISO527TensileStrain,break,50mm/min120%ISO527TensileModulus,1mm/min2150MPaISO527FlexuralStress,yield,2mm/min85MPaISO178FlexuralModulus,2mm/min2250MPaISO178IMPACTValueUnitStandardIzodImpact,notched,23°C88cm-kgf/cmASTMD256IzodImpact,notched,-30°C78cm-kgf/cmASTMD256InstrumentedImpactTotalEnergy,23°C714cm-kgfASTMD3763IzodImpact,unnotched80*10*3+23°CNBkJ/m2ISO180/1UIzodImpact,unnotched80*10*3-30°CNBkJ/m2ISO180/1UIzodImpact,notched80*10*3+23°C70kJ/m2ISO180/1AIzodImpact,notched80*10*3-30°C60kJ/m2ISO180/1ACharpy23°C,V-notchEdgew80*10*3sp=62mm70kJ/m2ISO179/1eACharpy-30°C,V-notchEdgew80*10*3sp=62mm65kJ/m2ISO179/1eACharpy23°C,UnnotchEdgew80*10*3sp=62mmNBkJ/m2ISO179/1eUCharpy-30°C,UnnotchEdgew80*10*3sp=62mmNBkJ/m2ISO179/1eUTHERMALValueUnitStandardVicatSofteningTemp,RateB/50145°CASTMD1525HDT,0.45MPa,3.2mm,unannealed139°CASTMD648HDT,1.82MPa,3.2mm,unannealed124°CASTMD648CTE,-40°Cto40°C,flow6.96E-051/°CASTME831CTE,-40°Cto40°C,xflow7.47E-051/°CASTME831CTE,23°Cto80°C,flow7.2E-051/°CISO11359-2CTE,23°Cto80°C,xflow7.2E-051/°CISO11359-2BallPressureTest,125°C+/-2°CPasses-IEC60695-10-2VicatSofteningTemp,RateB/50145°CISO306VicatSofteningTemp,RateB/120146°CISO306HDT/Be,0.45MPaEdgew120*10*4sp=100mm140°CISO75/BeHDT/Ae,1.8MPaEdgew120*10*4sp=100mm128°CISO75/AeRelativeTempIndex,Elec130°CUL746BRelativeTempIndex,Mechw/impact120°CUL746BRelativeTempIndex,Mechw/oimpact125°CUL746BPHYSICALValueUnitStandardSpecificGr***ity1.18-ASTMD792MoldShrinkage,flow,3.2mm0.4-0.8%SABICMethodMoldShrinkage,xflow,3.2mm0.4-0.8%SABICMethodMeltFlowRate,300°C/1.2kgf10g/10minASTMD1238Density1.19g/cm2ISO1183WaterAbsorption,(23°C/sat)0.35%ISO62MoistureAbsorption(23°C/50%RH)0.15%ISO62MeltVolumeRate,MVRat300°C/1.2kg9cm3/10minISO1133ELECTRICALValueUnitStandardVolumeResistivity>1.E+15Ohm-cmASTMD257SurfaceResistivity>1.E+15OhmASTMD257DielectricStrength,inoil,0.8mm16.2kV/mmASTMD149RelativePermittivity,100Hz2.68-ASTMD150RelativePermittivity,1MHz2.64-ASTMD150DissipationFactor,100Hz0.0012-ASTMD150DissipationFactor,1MHz0.0093-ASTMD150FLAMECHARACTERISTICSValueUnitStandardULRecognized,94HBFlameClassRating(3)0.4mmUL94GlowWireFlammabilityIndex850°C,passesat0.8mmIEC60695-2-12GlowWireFlammabilityIndex960°C,passesat1mmIEC60695-2-12GlowWireIgnitabilityTemperature,1.0mm875°CIEC60695-2-13GlowWireIgnitabilityTemperature,3.0mm875°CIEC60695-2-13如果您对我们的lexanPCEXL1414有任何疑问，或者想索取lexanPCEXL1414物性表datasheet、物质安全资料证书MSDS、ROHS检验报告、SGS报告、REACH环保证明、FDA证明、EU证明、UL证书及出厂证明COC/COA报告等，敬请拨打我们的服务电话，或者点击联系我们给我们留言。)