PA6BKV40---为了提高PA6的机械特性，经常加入各种各样的改性剂。玻璃就是***常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要受材料结晶度和吸湿性影响。Unitsystemtestmethodforphysicalpropertiesafterdryingandadjustmentproportion--1.46--g/cm³ASTMD79223°C1.46--g/cm³ISO1183Shrinkage:ISO2577Verticalflowdirection:280°C,3.00mm10.85--%ISO2577Verticalflowdirection:120°C,4hours,3.00mm20.070--%ISO2577Flowdirection:280°C,3.00mm30.16--%ISO2577Flowdirection:120°C,4hours,3.00mm40.030--%ISO2577WaterabsorptionISO62Saturated,23°C6.0--%ISO62Balanced,23°C,50%RH1.8--%ISO62Mechanicalproperties-unitsystemtestmethodafterdryingandadjustmentTensilemodulus23°C5118007400MPaASTMD63823°C119007800MPaISO527-2/1TensilestrengthFracture,23°C200120MPaASTMD638Fracture,23°C195130MPaISO527-2/5elongationFracture,23°C3.0%4.0%ASTMD638Fracture,23°C3.06.0%ISO527-2/5Bendingmodulus23°C108006800MPaASTMD79023°C6112007300MPaISO178/Abendingstrength23°C330200MPaASTMD7903.5%strain,23°C305170MPaISO178/A23°C7310200MPaISO178/AFlexuralStrainatFlexuralStrength8(23°C)4.05.0%ISO178/A)