PA6BG30X产品说明：PA6,30%glassfibers/glassspheres,injectionmolding,lowtendencytowarpPA6，30%玻璃纤维/玻璃球，注塑成型，低翘曲倾向Thermalproperties-unitsystemtestmethodafterdryingThermaldeformationtemperatureunderload0.45MPa,annealed,39.9MM200--°CASTMD6480.45MPa,annealed210--°CISO75-2/b1.8MPa,annealed190--°CISO75-2/a1.8MPa,annealed,3.99mm180--°CASTMD648Vicatsofteningtemperature>200--°CISO306/***,ISO306/b120Meltingtemperature10222--°CISO11357-3LinearcoefficientofthermalexpansionISO11359-2Flow:23to55°C3.0e-5--cm/cm/°CISO11359-2Transverse:23to55°C9.0e-5--cm/cm/°CISO11359-2RTIElec(1.50mm)120--°CUL746RTIImp(1.50mm)90.0--°CUL746RTI(1.50mm)125--°CUL746Electricalperformance-unitsystemtestmethodafterdryingandadjustingSurfaceresistivity:1.0e+14to1.0e+161.0e+12to1.0e+13ohmsIEC60093Volumeresistivity(23°C)1.0e+151.0e+11to1.0e+12ohms·cmIEC60093DielectricstrengthIEC60243-123°C,1.00mm3630kV/mmIEC60243-123°C,3.00mm3535kV/mmIEC60243-1DielectricconstantIEC6025023°C,50Hz114.5010.0IEC6025023°C,1MHz124.005.00IEC6025023°C,100Hz4.5016.0IEC6025023°C,1MHz4.004.80IEC60250DissipationfactorIEC6025023°C,50Hz0.0150.20IEC6025023°C,100Hz0.0130.31IEC6025023°C,1MHz0.0180.0200.100.060IEC60250Arcresistance13-110secASTMD495LeakagemarkindexSolutiona400-VIEC60112----450VASTMD3638TestmethodofunitsystemafterflammabilitydryingULflameretardantratingUL941.50mmHB--UL941.60mmHB--UL943.00mmHB--UL943.20mmHB--UL94Flammabilityindexofhotwire(2.00mm)650--°CIEC60695-2-12Limitoxygenindex1423--%ISO4589-2InjectiondryingunitsystemtestmethodDryingtemperature-dryairdryer80.0°CDryingtime-dryairdryer2.0to6.0HRProcessing(melt)temperature270to290°CMoldtemperature80.0to120°C)