PA61015GC6---1015gc6isapolyamide6(nylon6)productcontaining30%glassfiberreinforcement.ItcanbeprocessedbyinjectionmoldingandisavailableinNorthAmerica.Featuresinclude:Flameretardant/ratedflameChemicalresistancehighstrengthhardImpactresistanceThechemicalandphysicalpropertiesofpolyamide-6aresimilartonylon66,however,ithasalowmeltingpointandawiderangeofprocesstemperature.Itsimpactresistanceandsolubilityarebetterthannylon66plastics,butitsmoistureabsorptionisstronger.物理性能干燥调节后的单位制测试方法比重1.36--g/cm³ASTMD792收缩率-流动0.20到0.70--%ASTMD955吸水率(饱和)6.6--%ASTMD570硬度干燥调节后的单位制测试方法洛氏硬度ASTMD785M级100--ASTMD785R级120110ASTMD785机械性能干燥调节后的单位制测试方法抗张强度(屈服)16798.0MPaASTMD638伸长率(屈服)5.06.0%ASTMD638弯曲模量78404410MPaASTMD790弯曲强度(屈服)245127MPaASTMD790压缩强度27.415.7MPaASTMD695剪切强度85.258.8MPaASTMD732冲击性能干燥调节后的单位制测试方法悬壁梁缺口冲击强度ASTMD256-30°C78140J/mASTMD25623°C110230J/mASTMD256热性能干燥调节后的单位制测试方法载荷下热变形温度(1.8MPa,未退火)215--°CASTMD648熔融温度215到225--°C线形热膨胀系数-流动2.5E-5--cm/cm/°CASTMD696RTIElec(0.794mm)65.0--°CUL746RTIImp(0.794mm)65.0--°CUL746RTI(0.794mm)65.0--°CUL746电气性能干燥调节后的单位制测试方法体积电阻率1.0E+151.0E+12ohms·cmASTMD257介电常数ASTMD15060Hz4.20--ASTMD1501MHz3.80--ASTMD150耗散因数ASTMD15060Hz0.010--ASTMD1501MHz0.020--ASTMD150耐电弧性(0.794mm)121--secASTMD495可燃性干燥调节后的单位制测试方法UL阻燃等级(0.794mm)HB--UL94***干燥单位制建议的***大水分含量0.10%料筒后部温度240°C料筒中部温度265°C料筒前部温度275°C射嘴温度275°C加工（熔体）温度285°C模具温度70.0到80.0°C注塑压力83.2MPa背压9.80MPa螺杆转速100到130rpm)