PA6CM1017---Cm1017isapolyamide6(nylon6)product,.ItisavailableinNorthAmerica,EuropeorAsiaPacific.Themaincharacteristicsare:flameretardant/ratedflameUnitsystemtestmethodforphysicalpropertiesafterdryingandadjustmentDensity(23°C)1.13--g/cm3ISO1183Shrinkageflowdirectioninternalmethod1.00mm10.50to1.0--%internalmethod3.00mm21.0to1.6--%internalmethodWaterabsorptionISO6223°C,24hr1.8--%ISO62Saturated,23°C11--%ISO62Unitsystemtestmethodforhardness,dryingandadjustmentRockwellhardnessISO2039-2Rscale,80°C83--ISO2039-2Rscale,23°C11990ISO2039-2Mechanicalproperties-unitsystemtestmethodafterdryingandadjustmentTensilestressISO527-2-40°C120115MPaISO527-223°C85.040.0MPaISO527-280°C30.020.0MPaISO527-2TensilestrainISO527-2Yield,23°C1.5--%ISO527-2Fracture,23°C38.50%ISO527-2BendingmodulusISO178-40°C39003600MPaISO17823°C30001000MPaISO17880°C800400MPaISO178BendingstressISO178-40°C145140MPaISO17823°C12045.0MPaISO17880°C50.030.0MPaISO178Compressivestress(23°C)85.0--MPaISO604Shearstrength(23°C)75.0~70.0MPaASTMd732Taberabrasionresistance(1000cycles)3.00to4.00--MgISO9352Frictioncoefficient-vs.metal30.150to0.200--SuzukiMethodImpactperformance-unitsystemtestmethodafterdryingandadjustmentNotchedimpactstrengthofsimplysupportedbeamsISO179-40°C2.512kJ/m²ISO17923°C4.031kJ/m²ISO179NotchlessimpactstrengthofsimplysupportedbeamsISO179-Nofractureat40°C-ISO179Nofractureat23°C--ISO179Unitsystemtestmethodsforthermalperformance,dryingandconditioningHotdeformationtemperature(0.45MPa,UNannealed)190--CISO75-2/bMeltingtemperature:225--CDSCLinearcoefficientofthermalexpansion-flow8.0e-5--cm/cm/°CISO11359-2Specificheat1900--J/kg/℃Thermalconductivity:0.25--w/M/K)