PCPC-115奇美---Pc-115isapolycarbonate(PC)product,.ItcanbeprocessedbyinjectionmoldingandisavailableinNorthAmerica,AfricaandtheMiddleEast,LatinAmerica,EuropeorAsiaPacific.Featuresinclude:Flameretardant/ratedflamePassROHScertificationLowviscosity物理性能额定值单位制测试方法比重1.20g/cm³ASTMD792,ISO1183熔流率（熔体流动速率）(300°C/1.2kg)15g/10minASTMD1238溶化体积流率（MVR）(300°C/1.2kg)15.0cm³/10minISO1133收缩率ASTMD955流动0.50到0.70%ASTMD955横向流动0.50到0.70%ASTMD955吸水率(23°C,24hr)0.20%ASTMD570硬度额定值单位制测试方法洛氏硬度(M级)77ASTMD785球压硬度(H358/30)101MPaISO2039-1机械性能额定值单位制测试方法抗张强度屈服,3.18mm161.8MPaASTMD638屈服64.0MPaISO527-2/50断裂70.0MPaISO527-2/50伸长率屈服,3.18mm26.0%ASTMD638断裂,3.18mm3110%ASTMD638断裂120%ISO527-2/50弯曲模量6.35mm42350MPaASTMD790--52400MPaISO178弯曲强度6.35mm690.2MPaASTMD790--790.0MPaISO178压缩强度76.5MPaASTMD695冲击性能额定值单位制测试方法简支梁缺口冲击强度70kJ/m²ISO179悬壁梁缺口冲击强度3.18mm850J/mASTMD256--75kJ/m²ISO180/1A热性能额定值单位制测试方法载荷下热变形温度0.45MPa,未退火8136°CASTMD6481.8MPa,未退火9125°CASTMD6481.8MPa,未退火128°CISO75-2/A1.8MPa,退火143°CISO75-2/A维卡软化温度--150°CASTMD1525,ISO306/A50710--145°CISO306/***线形热膨胀系数-流动(44到100°C)6.0E-5到8.0E-5cm/cm/°CASTMD696导热系数0.20W/m/KASTMC177电气性能额定值单位制测试方法体积电阻率3.0E+16ohms·cmASTMD257介电强度(1.60mm)30kV/mmASTMD149介电常数ASTMD15060Hz2.95ASTMD1501MHz2.90ASTMD150耗散因数ASTMD15060Hz4.0E-4ASTMD1501MHz9.0E-3ASTMD150耐电弧性11110secASTMD495可燃性额定值单位制测试方法UL阻燃等级UL940.400mmV-2UL941.50mmV-2UL942.50mmV-2UL94光学性能额定值单位制测试方法折射率1.585ASTMD542透射率(76200µm)89.0%ASTMD1003雾度(81300µm)<0.80%ASTMD1003***额定值单位制干燥温度120°C干燥时间4.0hr料筒后部温度230到300°C料筒中部温度250到310°C料筒前部温度250到300°C模具温度70.0到120°C)