POMES-5日本宝理---Es-5isakindofPOMcopolymer,.ItcanbeprocessedbyinjectionmoldingandisavailableinNorthAmerica,EuropeorAsiaPacific.Typicalapplicationareas:automotiveindustry.Featuresinclude:Flameretardant/ratedflameConductivityAntistaticcarbonblack添加剂抗静电性碳黑(5%)特性导电抗静电性UL文件号E45034形式粒子加工方法***成型部件标识代码(ISO11469)>POM-CD5物理性能额定值单位制测试方法密度1.41g/cm³ISO1183熔流率（熔体流动速率）(190°C/2.16kg)9.0g/10minISO1133溶化体积流率（MVR）(190°C/2.16kg)8.00cm³/10minISO1133吸水率(23°C,24hr)1.3%ISO62硬度额定值单位制测试方法洛氏硬度(M计秤)90ISO2039-2机械性能额定值单位制测试方法拉伸模量2850MPaISO527-2拉伸应力49.0MPaISO527-2拉伸应变(断裂)7.5%ISO527-2弯曲模量2600MPaISO178弯曲应力84.0MPaISO178摩擦系数JISK7218Dynamic10.43JISK7218与钢-动态20.47JISK7218磨损因数JISK72180.98MPa,0.30m/sec3<1.010^-8mm³/N·mJISK72180.060MPa,0.15m/sec44010^-8mm³/N·mJISK72180.98MPa,0.30m/sec58010^-8mm³/N·mJISK72180.060MPa,0.15m/sec6120010^-8mm³/N·mJISK7218冲击性能额定值单位制测试方法简支梁缺口冲击强度3.0kJ/m²ISO179/1eA热性能额定值单位制测试方法热变形温度(1.8MPa,未退火)109°CISO75-2/A线形热膨胀系数内部方法流动:23到55°C1.1E-4cm/cm/°C内部方法横向:23到55°C1.1E-4cm/cm/°C内部方法电气性能额定值单位制测试方法表面电阻率5.0E+2ohms内部方法体积电阻率1.0E+2ohms·cm内部方法可燃性额定值单位制测试方法UL阻燃等级HBUL94补充信息额定值ColorNumberCD3501***额定值单位制干燥温度80.0到90.0°C干燥时间3.0到4.0hr加工（熔体）温度190到210°C模具温度60.0到80.0°C注塑压力49.0到98.0MPa螺杆转速100到150rpm)