巴斯夫PPSUUltrasonP3010是中等粘度注塑挤出级，具有良好的韧性和耐化学性（抗应力开裂），耐过热蒸汽。该特性曲线使其有可能用于高质量的技术部件和重型大批量产品。可采用热塑性塑料的常规加工方法。因此，UltrasonP3010可用于聚酰胺、聚碳酸酯、聚甲醛和聚对苯二甲酸亚烷基酯不再适用的场合，主要原因是热不稳定性或水解不稳定性。UltrasonP3010产品的性能谱允许替代硬质合金、金属和陶瓷。物理性能额定值(公制)额定值(英制)测试方法体积密度0.700-0.800g/cc0.0253-0.0289lb/in³密度1.29g/cc0.0466lb/in³ISO1183吸水率<=1.2%<=1.2%Equilibrium;ISO620.56%@Thickness2.00mm,Time180000sec0.56%@Thickness0.0787in,Time50.0hourStorage;ISO621.0%@Thickness2.00mm,Time360000sec1.0%@Thickness0.0787in,Time100hourStorage;ISO621.15%@Thickness2.00mm,Time1.08e+6sec1.15%@Thickness0.0787in,Time300hourStorage;ISO621.2%@Thickness2.00mm,Time1.80e+6sec1.2%@Thickness0.0787in,Time500hourStorage;ISO62平衡吸湿0.60%0.60%23°C;50%RH;ISO62水蒸气透过率100-150g/m²/day6.44-9.66g/100in²/dayDINEN12086粘度测量7171Viscositynumber;ISO1628线性成型收缩率,Flow0.0090cm/cm0.0090in/inISO294线性成型收缩率，横向0.010cm/cm0.010in/inISO294熔体流动速率>=45.15g/10min@Load10.0kg,Temperature360°C>=45.15g/10min@Load22.0lb,Temperature680°FISO1133机械性能额定值(公制)额定值(英制)测试方法球压硬度124MPa@Load36.5kg,Time30.0sec18000psi@Load80.5lb,Time0.00833hourISO2039-1抗张强度(断裂)74.0MPa10700psi5mm/min;ISO527-2抗张强度30.0MPa@Temperature160°C4350psi@Temperature320°F35.0MPa@Temperature160°C5080psi@Temperature320°F40.0MPa@Temperature23.0°C5800psi@Temperature73.4°F60.0MPa@Temperature23.0°C8700psi@Temperature73.4°F70.0MPa@Temperature23.0°C10200psi@Temperature73.4°F抗张强度(屈服)74.0MPa10700psi50mm/min;ISO527-245.0MPa@Temperature140°C6530psi@Temperature284°F55.0MPa@Temperature100°C7980psi@Temperature212°F65.0MPa@Temperature60.0°C9430psi@Temperature140°F75.0MPa@Temperature20.0°C10900psi@Temperature68.0°F伸长率(断裂)7.8%7.8%5mm/min;ISO527-2屈服伸长率7.8%7.8%50mm/min;ISO527-20.18%@Time36000sec,Pressure30.0MPa0.18%@Time10.0hour,Pressure4350psiISO8990.20%@Time3600sec,Pressure6.00MPa0.20%@Time1.00hour,Pressure870psi180°C;ISO8990.28%@Time36000sec,Pressure42.0MPa0.28%@Time10.0hour,Pressure6090psiISO8990.40%@Time3600sec,Pressure8.00MPa0.40%@Time1.00hour,Pressure1160psi180°C;ISO8990.50%@Pressure6.00MPa,Time360000sec0.50%@Pressure870psi,Time100hour180°C;ISO8990.50%@Time3600sec,Pressure10.0MPa0.50%@Time1.00hour,Pressure1450psiISO8990.51%@Pressure10.0MPa,Time36000sec0.51%@Pressure1450psi,Time10.0hourISO8990.52%@Pressure10.0MPa,Time360000sec0.52%@Pressure1450psi,Time100hourISO8990.53%@Pressure10.0MPa,Time3.60e+6sec0.53%@Pressure1450psi,Time1000hourISO8990.90%@Time3600sec,Pressure12.0MPa0.90%@Time1.00hour,Pressure1740psi180°C;ISO8991.0%@Time3600sec,Pressure14.0MPa1.0%@Time1.00hour,Pressure2030psi180°C;ISO8991.0%@Pressure6.00MPa,Time3.60e+6sec1.0%@Pressure870psi,Time1000hour180°C;ISO8991.0%@Pressure8.00MPa,Time360000sec1.0%@Pressure1160psi,Time100hour180°C;ISO8991.1%@Time3600sec,Pressure16.0MPa1.1%@Time1.00hour,Pressure2320psi180°C;ISO8991.1%@Time3600sec,Pressure20.0MPa1.1%@Time1.00hour,Pressure2900psiISO8991.2%@Time36000sec,Pressure20.0MPa1.2%@Time10.0hour,Pressure2900psiISO8991.25%@Pressure20.0MPa,Time360000sec1.25%@Pressure2900psi,Time100hourISO8991.28%@Pressure20.0MPa,Time3.60e+6sec1.28%@Pressure2900psi,Time1000hourISO8991.75%@Time3600sec,Pressure30.0MPa1.75%@Time1.00hour,Pressure4350psiISO8991.9%@Pressure8.00MPa,Time3.60e+6sec1.9%@Pressure1160psi,Time1000hour180°C;ISO8991.9%@Pressure12.0MPa,Time360000sec1.9%@Pressure1740psi,Time100hour180°C;ISO8991.95%@Pressure30.0MPa,Time360000sec1.95%@Pressure4350psi,Time100hourISO8992.1%@Pressure30.0MPa,Time3.60e+6sec2.1%@Pressure4350psi,Time1000hourISO8992.1%@Pressure14.0MPa,Time360000sec2.1%@Pressure2030psi,Time100hour180°C;ISO8992.5%@Time3600sec,Pressure40.0MPa2.5%@Time1.00hour,Pressure5800psiISO8992.6%@Time36000sec,Pressure40.0MPa2.6%@Time10.0hour,Pressure5800psiISO8992.7%@Pressure40.0MPa,Time360000sec2.7%@Pressure5800psi,Time100hourISO8992.75%@Time3600sec,Pressure42.0MPa2.75%@Time1.00hour,Pressure6090psiISO8993.0%@Pressure16.0MPa,Time360000sec3.0%@Pressure2320psi,Time100hour180°C;ISO8993.0%@Pressure40.0MPa,Time3.60e+6sec3.0%@Pressure5800psi,Time1000hourISO8993.0%@Pressure42.0MPa,Time360000sec3.0%@Pressure6090psi,Time100hourISO8993.2%@Pressure42.0MPa,Time3.60e+6sec3.2%@Pressure6090psi,Time1000hourISO8993.5%@Pressure12.0MPa,Time3.60e+6sec3.5%@Pressure1740psi,Time1000hour180°C;ISO8994.5%@Pressure14.0MPa,Time3.60e+6sec4.5%@Pressure2030psi,Time1000hour180°C;ISO8995.5%@Pressure16.0MPa,Time3.60e+6sec5.5%@Pressure2320psi,Time1000hour180°C;ISO899CreepStrength30.0MPa@Time3.60e+7sec4350psi@Time10000hourinwaterat95°C33.0MPa@Time3.60e+6sec4790psi@Time1000hourinwaterat95°C35.0MPa@Time360000sec5080psi@Time100hourinwaterat95°C37.0MPa@Time36000sec5370psi@Time10.0hourinwaterat95°C弹性模量1.60GPa@Temperature140°C232ksi@Temperature284°FISO5271.90GPa@Temperature100°C276ksi@Temperature212°FISO5272.10GPa@Temperature60.0°C305ksi@Temperature140°FISO5272.25GPa@Temperature20.0°C326ksi@Temperature68.0°FISO527拉伸模量>=2.27GPa>=329ksiISO527-2>=1.60GPa@Temperature140°C>=232ksi@Temperature284°FElasticity>=1.90GPa@Temperature100°C>=276ksi@Temperature212°FElasticity>=2.10GPa@Temperature60.0°C>=305ksi@Temperature140°FElasticity>=2.25GPa@Temperature20.0°C>=326ksi@Temperature68.0°FElasticity剪切模量0.200GPa@Temperature225°C29.0ksi@Temperature437°FISO67210.700GPa@Temperature200°C102ksi@Temperature392°FISO67210.750GPa@Temperature150°C109ksi@Temperature302°FISO67210.775GPa@Temperature100°C112ksi@Temperature212°FISO67210.800GPa@Temperature50.0°C116ksi@Temperature122°FISO6721)