PC基础创新塑料DMX2415--特性耐刮擦性外观半透明不透明可用颜色清晰/透明加工方法***成型PC基础创新塑料DMX2415产品说明：ThisproductwillbephasedoutperJanuary2015--LEXANDMX2415isapolycarbonateresinwithimprovedscratchresistance.LEXANDMX2415isavailableintransparent,translucent,andopaquecolors物理性能额定值单位制测试方法比重--1.20g/cm³ASTMD792--1.17g/cm³ISO1183,ASTMD792特定体积0.850cm³/gASTMD792硬度额定值单位制测试方法ErichsonScratchDepth-6N14.0µm内部方法PencilHardness1HASTMD3363物理性能额定值单位制测试方法熔流率（熔体流动速率）(300°C/1.2kg)15g/10minASTMD1238溶化体积流率（MVR）(300°C/1.2kg)13.5cm³/10minISO1133收缩率-流动(3.20mm)0.50到0.80%内部方法吸水率24hr0.080%ASTMD57024hr,50%RH0.040%ASTMD570饱和,23°C0.27%ISO62平衡,23°C0.28%ASTMD570平衡,50%RH0.13%ASTMD570平衡,23°C,50%RH0.13%ISO62硬度额定值单位制测试方法洛氏硬度ASTMD785L计秤108ASTMD785M级93ASTMD785球压硬度(H358/30)128MPaISO2039-1机械性能额定值单位制测试方法拉伸模量--22900MPaASTMD638--2450MPaISO527-2/1抗张强度屈服380.0MPaASTMD638屈服80.0MPaISO527-2/50断裂465.0MPaASTMD638断裂60.0MPaISO527-2/50伸长率屈服57.0%ASTMD638屈服7.0%ISO527-2/50断裂670%ASTMD638断裂40%ISO527-2/50弯曲模量50.0mm跨距72600MPaASTMD790--82450MPaISO178弯曲应力--108MPaISO178屈服,50.0mm跨距9120MPaASTMD790泰伯耐磨性1000Cycles,1000g,CS-17转轮10.0mg内部方法1000Cycles,1000g,CS-17转轮10.0mgASTMD1044薄膜额定值单位制测试方法透氧率(23°C)200000cm³·mm/m²/atm/24hrASTMF1307水气透过率(38°C,100%RH)0.90g·mm/m²/atm/24hrASTMF1249冲击性能额定值单位制测试方法简支梁缺口冲击强度10ISO179/1eA-30°C3.0kJ/m²ISO179/1eA23°C3.0kJ/m²ISO179/1eA简支梁无缺口冲击强度11ISO179/1eU-30°C47kJ/m²ISO179/1eU23°C无断裂ISO179/1eU悬壁梁缺口冲击强度-30°C30J/mASTMD25623°C30J/mASTMD256-30°C124.0kJ/m²ISO180/1A23°C135.0kJ/m²ISO180/1A无缺口悬臂梁冲击23°C无断裂ASTMD4812,ISO180/1U-30°C1445kJ/m²ISO180/1U装有测量仪表的落镖冲击(23°C,TotalEnergy)30.0JASTMD3763热性能额定值单位制测试方法载荷下热变形温度0.45MPa,未退火,3.20mm133°CASTMD6480.45MPa,未退火,64.0mm跨距15131°CISO75-2/Bf1.8MPa,未退火,3.20mm119°CASTMD6481.8MPa,未退火,64.0mm跨距16118°CISO75-2/Af维卡软化温度--139°CASTMD152517--138°CISO306/***--140°CISO306/B120BallPressureTestIEC60695-10-2125°CPassIEC60695-10-2140°C18PassIEC60695-10-2线形热膨胀系数流动:-40到95°C7.0E-5cm/cm/°CASTME831流动:23到80°C7.0E-5cm/cm/°CISO11359-2横向:-40到95°C7.0E-5cm/cm/°CASTME831横向:23到80°C7.0E-5cm/cm/°CISO11359-2比热1400J/kg/°CASTMC351导热系数0.20W/m/KASTMC177,ISO8302电气性能额定值单位制测试方法体积电阻率>1.0E+17ohms·cmASTMD257介电常数ASTMD15050Hz2.90ASTMD15060Hz2.90ASTMD1501MHz2.80ASTMD150相比耐漏电起痕指数(CTI)PLC2UL746可燃性额定值单位制测试方法UL阻燃等级(0.400mm)HBUL94光学性能额定值单位制测试方法折射率1.584ASTMD542,ISO489透射率(2540µm)88.0%ASTMD1003雾度(2540µm)<0.80%ASTMD1003***额定值单位制干燥温度120°C干燥时间3.0到4.0hr建议的***大水分含量0.020%料斗温度60.0到80.0°C料筒后部温度260到280°C料筒中部温度280到305°C料筒前部温度295到315°C射嘴温度290到310°C加工（熔体）温度295到315°C模具温度70.0到95.0°C)