PC沙伯基础955-701添加剂阻燃性特性ChlorineFree无***粘度，高阻燃性外观不透明可用颜色加工方法***成型PC沙伯基础955-701产品说明：Lexan*955Polycarbonate(PC)resinisanon-filled,injectionmoldablegrade.Thisnon-chlorinated,non-brominatedflameretardantPChasanUL-94V0ratingandisavailableinvariousopaquecoloropti***.Lexan955resinisofhighviscosityforvariousapplicati***物理性能额定值单位制测试方法比重1.19g/cm³ASTMD792熔流率（熔体流动速率）(300°C/1.2kg)7.0g/10minASTMD1238收缩率-流动(3.20mm)0.60到0.80%内部方法机械性能额定值单位制测试方法拉伸模量12280MPaASTMD638抗张强度2ASTMD638屈服62.1MPaASTMD638断裂65.5MPaASTMD638伸长率3ASTMD638屈服6.4%ASTMD638断裂130%ASTMD638弯曲模量4(50.0mm跨距)2340MPaASTMD790弯曲强度5(屈服,50.0mm跨距)101MPaASTMD790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度(23°C)800J/mASTMD256装有测量仪表的落镖冲击(23°C,TotalEnergy)73.4JASTMD3763热性能额定值单位制测试方法载荷下热变形温度ASTMD6480.45MPa,未退火,3.20mm138°CASTMD6481.8MPa,未退火,3.20mm127°CASTMD648维卡软化温度143°CASTMD15256线形热膨胀系数ASTME831流动:-40到40°C6.7E-5cm/cm/°CASTME831横向:-40到40°C6.7E-5cm/cm/°CASTME831RTIElec130°CUL746RTIImp120°CUL746RTI130°CUL746电气性能额定值单位制测试方法耐电弧性7PLC7ASTMD495相比耐漏电起痕指数(CTI)PLC2UL746高电弧燃烧指数(HAI)PLC3UL746高电压电弧起痕速率(HVTR)PLC4UL746热丝引燃(HWI)PLC2UL746可燃性额定值单位制测试方法UL阻燃等级UL940.8mmV-2UL941.5mmV-0UL943.1mm5VAUL94灼热丝***指数(1.0mm)960°CIEC60695-2-12热灯丝点火温度(1.0mm)850°CIEC60695-2-13***额定值单位制干燥温度121°C干燥时间3.0到4.0hr干燥时间，***大48hr建议的***大水分含量0.020%建议***量40到60%料筒后部温度288到310°C料筒中部温度299到321°C料筒前部温度310到332°C射嘴温度304到327°C加工（熔体）温度310到332°C模具温度82到116°C背压0.345到0.689MPa螺杆转速40到70rpm排气孔深度0.025到0.076mm)