原包朗盛PBTPocanB4225金先生159-1681-6001***1362174071PocanB4225000000PBT，20％玻璃纤维，注塑成型，阻燃应用：风扇罩，叶轮，印刷电路连接器，插头连接器，线轴，铁外壳密度1.57g/cc0.0567lb/in³ISO1183吸水率0.30%0.30%TestSim.toISO62平衡吸湿0.10%0.10%23°C/50%R.H.;TestSim.toISO62粘度测试97cm³/g97cm³/gViscositynumber;ISO307,1157,1628线性成型收缩率,Flow0.0049cm/cm0.0049in/inISO294-4,2577线性成型收缩率，横向0.0018cm/cm0.0018in/inISO294-4,2577简支梁无缺口冲击强度4.00J/cm²@Temperature-30.0°C19.0ft-lb/in²@Temperature-22.0°FISO179/1eU4.00J/cm²@Temperature23.0°C19.0ft-lb/in²@Temperature73.4°FISO179/1eU简支梁缺口冲击强度<=1.00J/cm²@Temperature-30.0°C<=4.76ft-lb/in²@Temperature-22.0°FISO179/1eA<=1.00J/cm²@Temperature23.0°C<=4.76ft-lb/in²@Temperature73.4°FISO179/1eA冲击628628Puncturemaximumforce(N);ISO6603-2多轴向仪器化冲击能量1.80J1.33ft-lbISO6603-2拉伸蠕变模量(1hr)7300MPa1.06e+6psiISO899-1拉伸蠕变模量(1000hr)6900MPa1.00e+6psiISO899-1电气性能额定值(公制)额定值(英制)测试方法体积电阻率>=1.00e+15ohm-cm>=1.00e+15ohm-cmIEC60093表面电阻>=1.00e+15ohm>=1.00e+15ohmIEC60093可燃性(UL94)V-2@Thickness0.800mmV-2@Thickness0.0315inIEC60695-11-10V-0@Thickness1.60mmV-0@Thickness0.0630inIEC60695-11-105VA@Thickness3.50mm5VA@Thickness0.138inIEC60695-11-20PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT结晶速度快，***适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.原包朗盛PBTPocanB4225)