导电PC瓷白PC物性表导电PC瓷白PC基本信息特性HighLightTran***ission良好的着色性流动性高用途光学应用加工方法***成型导电PC瓷白PC物理性能额定值单位制测试方法比重1.20g/cm³ASTMD792熔流率（熔体流动速率）(300°C/1.2kg)58g/10minASTMD1238收缩率-流动10.60到0.90%内部方法导电PC瓷白PC机械性能额定值单位制测试方法拉伸模量22230MPaASTMD638抗张强度3ASTMD638屈服61.0MPaASTMD638断裂59.0MPaASTMD638伸长率4ASTMD638屈服7.0%ASTMD638断裂120%ASTMD638弯曲模量5(50.0mm跨距)2420MPaASTMD790弯曲强度6(屈服,50.0mm跨距)97.0MPaASTMD790导电PC瓷白PC冲击性能额定值单位制测试方法悬壁梁缺口冲击强度ASTMD256-30°C44J/mASTMD25623°C580J/mASTMD256无缺口悬臂梁冲击(23°C)2100J/mASTMD4812装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad)56.0JASTMD3763导电PC瓷白PC热性能额定值单位制测试方法载荷下热变形温度ASTMD6480.45MPa,未退火,3.20mm139°CASTMD6481.8MPa,未退火,3.20mm124°CASTMD648维卡软化温度142°CISO306/B120线形热膨胀系数ASTME831流动:-40到95°C6.8E-5cm/cm/°CASTME831横向:-40到95°C6.6E-5cm/cm/°CASTME831导电PC瓷白PC光学性能额定值单位制测试方法透射率(2540µm)>90.0%ASTMD1003导电PC瓷白PC***额定值单位制干燥温度121°C干燥时间3.0到4.0hr干燥时间，***大48hr建议的***大水分含量0.020%建议***量40到60%料筒后部温度271到293°C料筒中部温度282到304°C料筒前部温度293到316°C射嘴温度288到310°C加工（熔体）温度293到316°C模具温度71.1到93.3°C背压0.345到0.689MPa螺杆转速40到70rpm排气孔深度0.025到0.076mm备注1.TensileBar2.50mm/min3.类型1,50mm/min4.类型1,50mm/min5.1.3mm/min6.1.3mm/min)