LNP™STAT-KON™9X02785compound聚碳酸酯专有填料产品说明:总体填料/增强材料专有填料特性导电加工方法***成型物理性能额定值单位制测试方法比重ASTMD792--1.27g/cm³--1.26g/cm³收缩率ASTMD955流动:24小时0.40到0.70%横向流动:24小时0.50到0.80%吸水率24hr,50%RH0.091%ASTMD570平衡,23°C,50%RH0.14%ISO62机械性能额定值单位制测试方法拉伸模量--22850MPaASTMD638--2760MPaISO527-2/1抗张强度屈服64.1MPaASTMD638屈服363.0MPaASTMD638屈服56.0MPaISO527-2/5断裂352.0MPaASTMD638断裂52.0MPaISO527-2/5伸长率屈服34.3%ASTMD638屈服2.9%ISO527-2/5断裂4.0%ASTMD638断裂37.8%ASTMD638断裂3.1%ISO527-2/5弯曲模量50.0mm跨距42920MPaASTMD790--2900MPaASTMD790--52800MPaISO178弯曲强度--103MPaASTMD790--96.0MPaISO178屈服,50.0mm跨距4107MPaASTMD790断裂,50.0mm跨距475.9MPaASTMD790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度23°C60J/mASTMD25623°C67.1kJ/m²ISO180/1A无缺口悬臂梁冲击23°C2200J/mASTMD481223°C6150kJ/m²ISO180/1U装有测量仪表的落镖冲击23°C,TotalEnergy35.7JASTMD3763--35.4JISO6603-2热性能额定值单位制测试方法载荷下热变形温度0.45MPa,未退火,3.20mm117°CASTMD6480.45MPa,未退火,64.0mm跨距7114°CISO75-2/Bf1.8MPa,未退火,3.20mm106°CASTMD6481.8MPa,未退火,64.0mm跨距7103°CISO75-2/Af线形热膨胀系数ASTMD696流动:-30到30°C6.8E-5cm/cm/°C横向:-30到30°C6.8E-5cm/cm/°C电气性能额定值单位制测试方法表面电阻率1.0E+2到1.0E+5ohmASTMD257体积电阻率1.0E+2到1.0E+7ohm·cmASTMD257***额定值单位制干燥温度121°C干燥时间4.0hr建议的***大水分含量0.020%料筒后部温度293到304°C料筒中部温度310到321°C料筒前部温度321到332°C加工（熔体）温度304到327°C模具温度82.2到110°C背压0.172到0.344MPa螺杆转速30到60rpm)