LEXAN™9945Aresin聚碳酸酯产品说明:总体添加剂阻燃性特性ChlorineFree通用无***阻燃性用途薄壁部件通用外观清晰/透明加工方法***成型物理性能额定值单位制测试方法比重1.20g/cm³ASTMD792,ISO1183熔流率（熔体流动速率）(300°C/1.2kg)10g/10minASTMD1238收缩率内部方法流动:3.20mm0.50到0.70%横向流动:3.20mm0.50到0.70%吸水率ISO62饱和,23°C0.35%平衡,23°C,50%RH0.15%硬度额定值单位制测试方法球压硬度(H358/30)95.0MPaISO2039-1机械性能额定值单位制测试方法拉伸模量--22380MPaASTMD638--2350MPaISO527-2/1抗张强度屈服364.0MPaASTMD638屈服63.0MPaISO527-2/50断裂366.0MPaASTMD638断裂65.0MPaISO527-2/50伸长率屈服36.0%ASTMD638屈服6.0%ISO527-2/50断裂3120%ASTMD638断裂100%ISO527-2/50弯曲模量50.0mm跨距42450MPaASTMD790--52300MPaISO178弯曲应力--5,690.0MPaISO178屈服,50.0mm跨距4102MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度7ISO179/1eA-30°C14kJ/m²23°C73kJ/m²简支梁无缺口冲击强度7ISO179/1eU-30°C无断裂23°C无断裂悬壁梁缺口冲击强度-30°C110J/mASTMD25623°C820J/mASTMD256-30°C812kJ/m²ISO180/1A23°C870kJ/m²ISO180/1A无缺口伊佐德冲击强度8ISO180/1U-30°C无断裂23°C无断裂装有测量仪表的落镖冲击(23°C,TotalEnergy)79.0JASTMD3763热性能额定值单位制测试方法载荷下热变形温度0.45MPa,未退火,3.20mm138°CASTMD6480.45MPa,未退火,100mm跨距9136°CISO75-2/Be1.8MPa,未退火,3.20mm127°CASTMD6481.8MPa,未退火,100mm跨距9125°CISO75-2/Ae维卡软化温度--143°CASTMD152510--141°CISO306/***--142°CISO306/B120BallPressureTest(125°C)PassIEC60695-10-2线形热膨胀系数流动:-40到40°C6.8E-5cm/cm/°CASTME831流动:23到80°C7.0E-5cm/cm/°CISO11359-2横向:-40到40°C7.3E-5cm/cm/°CASTME831横向:23到80°C7.0E-5cm/cm/°CISO11359-2导热系数0.20W/m/KISO8302电气性能额定值单位制测试方法表面电阻率>1.0E+15ohmIEC60093体积电阻率>1.0E+15ohm·cmIEC60093介电强度(3.20mm,在油中)17kV/mmIEC60243-1相对电容率IEC6025050Hz2.7060Hz2.701MHz2.70耗散因数IEC6025050Hz1.0E-360Hz1.0E-31MHz0.010漏电起痕指数225VIEC60112可燃性额定值单位制测试方法UL阻燃等级UL940.800mmV-21.80mmV-0灼热丝***指数(1.00mm)960°CIEC60695-2-12热灯丝点火温度IEC60695-2-131.00mm850°C3.00mm850°C极限氧指数35%ISO4589-2光学性能额定值单位制测试方法透射率(2540µm)88.0%ASTMD1003雾度(2540µm)1.0%ASTMD1003***额定值单位制干燥温度120°C干燥时间2.0到4.0hr建议的***大水分含量0.020%料斗温度60.0到80.0°C料筒后部温度260到280°C料筒中部温度270到290°C料筒前部温度280到310°C射嘴温度270到290°C加工（熔体）温度280到310°C模具温度80.0到110°C)