加纤PC挤出PC物性表加纤PC挤出PC基本信息特性HighLightTran***ission良好的颜色稳定性流动性高用途光学应用加工方法***成型加纤PC挤出PC物理性能额定值单位制加纤PC挤出PC测试方法比重1.20g/cm³ASTMD792熔流率（熔体流动速率）(300°C/1.2kg)38g/10minASTMD1238收缩率-流动10.60到0.90%内部方法加纤PC挤出PC机械性能额定值单位制加纤PC挤出PC测试方法拉伸模量22200MPaASTMD638抗张强度3ASTMD638屈服62.0MPaASTMD638断裂63.0MPaASTMD638伸长率4ASTMD638屈服7.0%ASTMD638断裂130%ASTMD638弯曲模量5(50.0mm跨距)2360MPaASTMD790弯曲强度6(屈服,50.0mm跨距)98.0MPaASTMD790加纤PC挤出PC冲击性能额定值单位制加纤PC挤出PC测试方法悬壁梁缺口冲击强度ASTMD256-30°C80J/mASTMD25623°C670J/mASTMD256无缺口悬臂梁冲击(23°C)2100J/mASTMD4812装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad)63.0JASTMD3763加纤PC挤出PC热性能额定值单位制加纤PC挤出PC测试方法载荷下热变形温度ASTMD6480.45MPa,未退火,3.20mm139°CASTMD6481.8MPa,未退火,3.20mm127°CASTMD648维卡软化温度143°CISO306/B120线形热膨胀系数ASTME831流动:-40到95°C6.4E-5cm/cm/°CASTME831横向:-40到95°C6.7E-5cm/cm/°CASTME831加纤PC挤出PC光学性能额定值单位制加纤PC挤出PC测试方法透射率(2540µm)>90.0%ASTMD1003加纤PC挤出PC***额定值单位制加纤PC挤出PC干燥温度121°C干燥时间3.0到4.0hr干燥时间，***大48hr建议的***大水分含量0.020%建议***量40到60%料筒后部温度271到293°C料筒中部温度282到304°C料筒前部温度293到316°C射嘴温度288到310°C加工（熔体）温度293到316°C模具温度71.1到93.3°C背压0.345到0.689MPa螺杆转速40到70rpm排气孔深度0.025到0.076mm备注1.TensileBar2.50mm/min3.类型1,50mm/min4.类型1,50mm/min5.1.3mm/min6.1.3mm/min)