LEXAN™143Xresin物性表聚碳酸酯产品说明:ImprovedflowPCwithexcellentprocessabilityandmoldrelease.总体添加剂脱模特性可加工性，良好良好的流动性加工方法***成型物理性能额定值单位制测试方法比重1.20g/cm³ASTMD792,ISO1183熔流率（熔体流动速率）(300°C/1.2kg)12g/10minASTMD1238收缩率-流动(3.20mm)0.40到0.80%内部方法吸水率ISO62饱和,23°C0.35%平衡,23°C,50%RH0.15%机械性能额定值单位制测试方法拉伸模量--22320MPaASTMD638--2450MPaISO527-2/1抗张强度屈服360.0MPaASTMD638屈服60.0MPaISO527-2/50断裂360.0MPaASTMD638断裂59.0MPaISO527-2/50伸长率屈服36.0%ASTMD638屈服6.0%ISO527-2/50断裂3120%ASTMD638断裂120%ISO527-2/50弯曲模量50.0mm跨距42360MPaASTMD790--52310MPaISO178弯曲应力--5,690.0MPaISO178屈服,50.0mm跨距486.0MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度7ISO179/1eA-30°C12kJ/m²23°C65kJ/m²简支梁无缺口冲击强度7ISO179/1eU-30°C无断裂23°C无断裂悬壁梁缺口冲击强度-30°C240J/mASTMD25623°C830J/mASTMD256-30°C811kJ/m²ISO180/1A23°C865kJ/m²ISO180/1A无缺口伊佐德冲击强度8ISO180/1U-30°C无断裂23°C无断裂装有测量仪表的落镖冲击(23°C,TotalEnergy)72.0JASTMD3763热性能额定值单位制测试方法载荷下热变形温度1.8MPa,未退火,3.20mm128°CASTMD6481.8MPa,未退火,6.40mm129°CASTMD6481.8MPa,未退火,64.0mm跨距9122°CISO75-2/Af维卡软化温度--141°CASTMD152510,ISO306/***10--143°CISO306/B120线形热膨胀系数ASTME831,ISO11359-2流动:-40到40°C6.0E-5cm/cm/°C横向:-40到40°C6.0E-5cm/cm/°C***额定值单位制干燥温度121°C干燥时间3.0到4.0hr干燥时间，***大48hr建议的***大水分含量0.020%建议***量40到60%料筒后部温度271到293°C料筒中部温度282到304°C料筒前部温度293到316°C射嘴温度288到310°C加工（熔体）温度293到316°C模具温度71.1到93.3°C背压0.345到0.689MPa螺杆转速40到70rpm排气孔深度0.025到0.076mm)